| Nylon 66 high tenacity yarn |
| |
| The products are used predominantly as a reinforcement material in the tyre industry, particularly in those sectors of the tyre market where the superior impact recovery properties of nylon are required. Other outlets are to be found in the conveyor belt, coated substrate and rope industries. |
| |
| Items |
Unit |
840D(940dtex) |
1260D(1400dtex) |
1680D(1880dtex) |
1890D(2100dtex) |
| Tensile strength |
GPD |
MIN 9.5 |
MIN 9.5 |
MIN 9.5 |
MIN 9.5 |
| Linear density |
dtex |
±20 |
±30 |
±35 |
±40 |
| Elongation at break |
% |
19.0±3 |
19.0±3 |
19.0±3 |
19.0±3 |
| CV of linear density |
% |
MAX 0.5 |
MAX 0.5 |
MAX 0.5 |
MAX 0.5 |
| CV of breaking strength |
% |
MAX 2.0 |
MAX 2.0 |
MAX 2.0 |
MAX 2.0 |
| CV of elongation at break |
% |
MAX 3.0 |
MAX 3.0 |
MAX 3.0 |
MAX 3.0 |
| Heat shrinkage |
% |
6.0±2(177℃×2m) |
6.0±2(177℃×2m) |
6.0±2(177℃×2m) |
6.0±2(177℃×2m) |
| Percentage of UV |
% |
2.0 |
2.0 |
2.0 |
2.0 |
|
| |
| Items |
Unit |
210D |
420D |
630D |
| Tensile strength |
GPD |
MIN8.5 |
MIN8.5 |
MIN8.5 |
| Elongation at break |
% |
19±3 |
19±3 |
19±3 |
| CV of linear density |
% |
MAX 2.0 |
MAX 2.0 |
MAX 2.0 |
| CV of breaking strength |
% |
MAX 6.0 |
MAX 6.0 |
MAX 6.0 |
| CV of elongation at break |
% |
MAX 15.0 |
MAX 15.0 |
MAX 15.0 |
| Heat shrinkage |
% |
6.5±1(180℃×15m) |
6.5±1(180℃×15m) |
6.5±1(180℃×15m) |
| Percentage of UV |
% |
2.0 |
2.0 |
|
|
| High tenacity,raw white,UV-stabilized |
|
|
| | Close | |
|
| |
|
![]() |
|
|
|