| Adhesive activated to rubber yarn |
| |
| NO |
Product code |
Linear density
Denier |
Filament count |
Tenacity |
Elongation
(%) |
H.A.S(%)
177/1/0.05 |
AD-ACT
FOY
(%) |
FOY
(%) |
Intermi-ngle n/m |
Bobbin Dimension（mm） |
| cN/dtex |
G/D |
Type 1
11 kg |
Type 2
10 kg |
Type 3
5.5 kg |
| |
|
|
|
|
|
|
|
|
|
|
| 1 |
GHT04 |
420 ± 3% |
96 |
≥7.9 |
≥8.9 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
2～7 |
|
|
260 |
| 2 |
GHT05 |
500 ± 3% |
96 |
≥7.9 |
≥8.9 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
2～7 |
|
|
260 |
| 3 |
GHT84 |
840 ± 3% |
192 or96 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
2～7 |
270 |
260 |
260 |
| 4 |
GHT10 |
1000 ± 3% |
192 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
2～7 |
270 |
260 |
|
| 5 |
GHT13 |
1300 ± 3% |
192 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
2～7 |
270 |
260 |
|
| 6 |
GHT15 |
1500 ± 3% |
192 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
2～7 |
270 |
260 |
|
| 7 |
GHT20 |
2000 ± 3% |
384 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
0～4 |
270 |
260 |
|
| 8 |
GHT25 |
2500 ± 3% |
384 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0
.15 |
0～4 |
270 |
260 |
|
| 9 |
GHT30 |
3000 ± 3% |
384 |
≥8.0 |
≥9.0 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
0～4 |
270 |
260 |
|
| 10 |
GHT40 |
4000 ± 3% |
768 |
≥7.9 |
≥8.9 |
13.5±2.0 |
8.0±1.5 |
0.6±
0.15 |
0.6±
0.15 |
0～4 |
270 |
260 |
|
|
| * The Adhesive Activated Yarn: For The Rubber Adhesion Improvement In Single-dip Process |
| |
| Main Applications : |
| V-belt - Hoisting Cable - Tie Down - Rubber Thread Rope - Cordage -Rubber Folding Core Thread - Geotextile Geogrid |
| Canvas-- Meridian Cloth, Conveyor belts - Transmission belts - Another engineering reinforcement |
|
|
| |
| Remarks : |
| 1. Tenacity Test Machine : XFDQ-WGJ-2500B1 |
3. Testing Method：GB/T 14344 & DIN 53840 |
| 2. H.A.S - Hot Air Shrinkage : 177℃-1min - 0.05g/D |
4. Quality Standard : ISO-9001(Q.M.S); |
|
|
| |
|
| | Close | |
|
| |
|
![]() |
|
|
|